作者： Aleksei V. Kubarkov1, Olga A. Pyshkina1, Evgeny A. Karpushkin1, Keith J. Stevenson2, Vladimir G. Sergeyev1

1.Faculty of Chemistry, Lomonosov Moscow State University, Moscow, Russia

2.Skolkovo Institute of Science and Technology, Moscow, Russia

 

摘要：Oxidative chemical polymerization of 3,4-ethylenedioxythiophene was carried with 5.8-μm sulfonated polystyrene latex particles as template. Polymerization led to formation of poly(3,4-ethylenedioxythiophene) distributed over the surface of template particles. Increase in initial monomer concentration resulted in the change of poly(3,4-ethylenedioxythiophene) morphology from isolated clusters to continuous 0.2–0.5-μm-thick surface shells. Structure of poly(3,4-ethylenedioxythiophene) coatings had crucial influence on the surface charge and macroscopic electrical conductivity of composite latex particles.